Comparative analysis of slag pot production materials

20 Feb,2019 UTC+8 Views:


Many people in the industry understand that metallurgical slag pot are one of the auxiliary equipment in the metallurgical industry. They are used for steelmaking or ironmaking slag or waste. Because of the high temperature slag required, manufacturers have high requirements on the material of the slag pot. Previously, the traditional slag pot materials were made of ductile iron or cast steel. Most of the materials are now cast from cast steel.

Xinxiang Great Wall cast steel is mainly based on cast steel equipment, and its hunting industry is also more, there are five major industries such as metallurgical industry, building materials industry, ceramic industry, construction industry and forging industry. Until now, it has a history of more than 60 years. As the productivity increases, the scale will continue to expand. It has already occupied a certain proportion in the domestic market and can be customized according to the drawings of customers. After decades of efforts, Great Wall Cast Steel has accumulated a large amount of experience in tracking and researching the use of the entire industry and products. It is also strictly required for technical aspects, and experts are invited to conduct training on a regular basis. Great Wall Cast Steel is a relatively professional and reliable manufacturer on metallurgical slag pots.

Then what are the characteristics of spheroidal graphite cast iron and cast steel slag pots:

1. Comparison of performance: The tensile strength of the slag slag pot is greater than or equal to 400mpa, the strength is high, and the high impact resistance is also strong; the tensile strength of the cast steel slag pot is also greater than or Is equal to 400mpa;

2. Comparison of heat resistance: The ductile iron slag pot itself has good moldability and is more resistant to heat and fatigue; the cast steel slag pot is also plastic, and the crack is particularly rare in the case of extremely cold and extremely hot. of;

3, deformation degree comparison: ductile iron slag pot is not easy to deform; cast steel slag pot is not particularly easy to deform;

4, crack comparison: the spheroidal graphite cast iron slag can appear in the local crack, and continue to use; the material of the cast steel slag pot is not prone to cracks, if it can be welded to make up;